DEGREE OF CONVERSION, AND COMPRESSIVE STRENGTH OF RECENTLY INTRODUCED DENTAL COMPOSITES AS A CORE BUILD-UP MATERIALS
DEGREE OF CONVERSION, AND COMPRESSIVE STRENGTH OF RECENTLY INTRODUCED DENTAL COMPOSITES AS A CORE BUILD-UP MATERIALS
 
لغة الوثيقة : الانجليزية 
المستخلص : This study was conducted to determine the degree of conversion (DC) and compressive strength of new dental composites used as a core build-up materials in comparison to hybrid types. Fourier transform infrared Analysis (FTIR) method was utilized in this study as a documented method to measure the degree of conversion. DC was calculated by comparing the absorbarice ratio ofaliphatic C=C peak at 1638 cm-I to aromatic C=C peak at 1608 cm-l between cured and uncured specimens. The DC % was calculated by subtractirrg the residual percentage of uncured methacrylate from 100%. Also compressive strength test was conducted for selected materials. Results of this study indicated that DC ranged from 43.7 (For Herculite) to 74.1 (for Admira). The compressive strength ranged from 264 MPa (for Admira)to 442 MPa (for ZI00). No positive correlation was noticed between both results which may be attributed to "many factors such as material composition (organic & inorganic) and light irradiation conditions. 
ردمد : 0 
اسم الدورية : المجلة المصرية لطب الأسنان 
المجلد : 47 
العدد : 3 
سنة النشر : 2001 هـ
2001 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, December 10, 2007 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
عبد الحميد مغربيMaghrabi, Abdulhamid باحث رئيسيدكتوراهamaghrabi@kau.edu.sa
محمد عوضAwad, Mohamed باحث مشاركدكتوراه 
محمد شحاتهShehata, Mohamed باحث مشاركدكتوراه 

الملفات


تحميل الصفحة

الرجوع إلى صفحة الأبحاث