COMPRESSIVE STRENGTH, SOLUBILITY AND MICRO-LEAKAGE OF FLAX FIBRES REINFORCED ZINC OXIDE EUGENOL DENTِAL CEMENT MATERIAL
COMPRESSIVE STRENGTH, SOLUBILITY AND MICRO-LEAKAGE OF FLAX FIBRES REINFORCED ZINC OXIDE EUGENOL DENTِAL CEMENT MATERIAL
 
لغة الوثيقة : الانجليزية 
المستخلص : This work was carried out to improve properties of soft zinc oxide Eugenal (ZOE) as dental cement material, This was realized by reinforcement of ZOE with flax fibers . The results indicated that adding this natural material at 0,1% and 0.2% by weight gave good and promissing results over untreated checks. Significant increase in compressive strenght with 0.1% and 0.2% of flax fibres over control. Solubility precentage showed insignificant tendency to decrease owing to flax fibres applications. Micro-leakage decreased significantly with increasingn flax fibers up to 0.2% . These results indicate that reinforcement of ZOE with cellulosic flax fibres improved properties of ZOE with regard to compressive strength, solubility and micro-leakge as dental cement material. 
ردمد : 0 
اسم الدورية : Flax and other bast plants Symp 
المجلد : 1 
العدد : 1 
سنة النشر : 1997 هـ
1997 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Wednesday, June 18, 2008 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
محمد محمدmuhammad, Muhammad باحث رئيسيدكتوراهmmmuhammad@kau.edu.sa

الملفات


تحميل الصفحة

الرجوع إلى صفحة الأبحاث