ELECTRO-CHEMICAL BEHA VIOR AND SURFACE HARDNESS OF SELECTED
ELECTRO-CHEMICAL BEHA VIOR AND SURFACE HARDNESS OF SELECTED
 
لغة الوثيقة : الانجليزية 
المستخلص : The aim of this study was to determine the corrosion behavior of commercial nickel-chromium and cobalt chromium alloys in different pH media. Also hardness tests were performed for surface mechanical properties evaluation. Two Ni-Cr (Ugirex-III and Wiron 88) and three Co-Cr alloys (Remanium 2000, Wironium & Wironit LA) were investigated by electrochemical technique (Potentiodynamic test) using potentiostat (HAG 5001) in o.g. mass % NaCI solutions of pHs 1.3, 4.4 & 7 at room temperature. Vickers hardness and Rockwell hardness were performed for these alloys. The three Co-Cr alloys revealed high corrosion resistance, especially, Remanium alloy at different pH solutions in comparison with Ni-Cl' alloys (Wiron 88, showed sever dissolution in any pH medium i.e it is the most corrodible alloy). The two Ni-Cr alloys showed lower hardness values than Co-Cr alloys. It was concluded that, harder Co-Cr alloys showed higher corrosion resistance than softer Ni-Cr alloys tested in this study. There may be a direct correlation between surface hardness property and corrosion resistance in general. 
ردمد : 0 
اسم الدورية : المجلة المصرية لطب الأسنان 
المجلد : 47 
العدد : 3 
سنة النشر : 2001 هـ
2001 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Tuesday, May 20, 2008 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
محمد محمدmuhammad, Muhammad باحث رئيسيدكتوراهmmmuhammad@kau.edu.sa

الملفات


تحميل الصفحة

الرجوع إلى صفحة الأبحاث