TiO2 nanoparticles with tetra-pad shape prepared by an economical and safe route at very low temperature
TiO2 nanoparticles with tetra-pad shape prepared by an economical and safe route at very low temperature
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : We report an organics free and safe route for the preparation of titanium dioxide (TiO2) nanoparticles having tetrapad shape. The approach is based on a very simple reaction of titanium powder and de-ionized water at very low temperatures of ~140°C without using any organics or surfactants. By the morphological investigations using FESEM and HRTEM, it was observed that the grown products are having tetrapad shape with the diameters in the range of 10-50nm. The EDS and XRD pattern confirmed the composition and crystallinity of the grown nanoparticles and revealed that the grown products are pure TiO2 with the tetragonal anatase phase. Since only water, which is regarded as a benign solvent is used during the preparation of nanoparticles, we believe that the product so produced is biocompatible and bio-safe and can be readily used for food and medicine. Besides other advantages, the present method is economical, fast, low temperature, free of pollution and environmentally benign which will make it suitable for large scale production. 
ردمد : 1913-1844 
اسم الدورية : Modern Applied Science 
المجلد : 5 
العدد : 3 
سنة النشر : 1432 هـ
2011 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Saturday, February 11, 2012 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
ليلى محمد الحربيAl-Harbi, Liala Mohammadباحثدكتوراهlmajeed2002@yahoo.com
السيد حسيني المسلميEl-Mossalamy, El-sayed Hباحثدكتوراهsbdmina@yahoo.com
H M ArafaArafa, H Mباحثدكتوراهhan.m.a.2008@hotmail.com
Ahmad A Al-OwaisAl-Owais, Ahmad Aباحثدكتوراهaowais21@yahoo.com
محمد أشرف شاهShah, Mohammad Ashrafباحثدكتوراهshahkau@hotmail.com

الملفات

اسم الملفالنوعالوصف
 32229.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث