Synthesis and field emission properties of nickel oxide nanoplatelets prepared by simple novel technique
Synthesis and field emission properties of nickel oxide nanoplatelets prepared by simple novel technique
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : Single crystalline NiO nanoplatelets were successfully synthesized by new facile method at 200 °C. The morphology and microstructure were determined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). XRD measurement indicated that the prepared sample had typical cubic structures. The SEM investigation confirmed that the product was of the form of nanoplatelets. These nanoplatelets have average width length 250 nm and thickness of 20 nm. The field emission measurements demonstrate that the NiO nanoplatelets show a promising field emission property. The improved field emission is attributed to the local field enhancement factor at the nanoplatelets. The results confirm the importance of the morphology of nanomaterial in field emission. 
ردمد : 0749-6036 
اسم الدورية : Superlattices and Microstructures 
المجلد : 50 
العدد : 1 
سنة النشر : 1432 هـ
2011 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Wednesday, February 8, 2012 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
وليد السيد محمودMahmoud, Waleed Eباحثدكتوراهw_e_mahmoud@yahoo.com
طلال صدقة الحربيAl-Harbi, Talal Sباحثدكتوراهtharbi1@yahoo.com

الملفات

اسم الملفالنوعالوصف
 32227.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث