Structure and optoelectronic properties of PbSe quantum dots /PVA. Does the polymer molecular weight matter?
Structure and optoelectronic properties of PbSe quantum dots /PVA. Does the polymer molecular weight matter?
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : Polyvinyl alcohol (PVA) with different molecular weights (8000, 14,000, and 132,000g/mol) capped lead selenide (PbSe) quantum dots (QDs) are prepared. The nanocomposites are characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). XRD and TEM studies show that the particle size of PbSe QDs decrease with the increase in PVA molecular weight and/or PVA amount. This may be due to the increase in molecular weight inhibiting further growth of PbSe into the polymer matrix. Thermogravimetric analysis showed that the introduction of PbSe QDs into PVA decreases the crystallinity of the polymer. The optical absorption spectroscopy of prepared nanocomposites showed that the absorption peaks are strongly shifted to the lower wavelength (blue shift) from near infrared region to visible region by increasing the PVA molecular weight. The (I-V) characteristic curves of the PVA/PbSe nanocomposite films under illumination showed a photovoltaic cell-like behavior. The results indicated that as the molecular weight of polymer increases, the conversion efficiency increases. 
ردمد : 1042-7147 
اسم الدورية : Polymers for Advanced Technologies 
المجلد : 22 
العدد : 12 
سنة النشر : 1432 هـ
2011 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Wednesday, February 8, 2012 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
وليد السيد محمودMahmoud, Waleed Eباحثدكتوراهw_e_mahmoud@yahoo.com

الملفات

اسم الملفالنوعالوصف
 32222.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث