Synthesis, characterization and photoluminescence properties of Sn doped ZnO nanonails
Synthesis, characterization and photoluminescence properties of Sn doped ZnO nanonails
 
الموضوع : فيزياء 
لغة الوثيقة : الانجليزية 
المستخلص : Vertically aligned undoped ZnO nanowires and Sn doped ZnO nanonails are synthesized on a silicon substrate using vaporsolid technique, without using a catalyst or predeposited buffer layers. The structure and morphology of the as-synthesized nanonails and nanowires are characterized using X-ray diffraction, scanning electron microscopy, transmission electron microscopy, selected area electron diffraction, and electron dispersive X-ray spectroscopy. The results showed that the use of SnCl 2 is critical for the formation of nanonails. Without it, only ZnO nanowires can be obtained. The photoluminescence properties are also investigated at room temperature. The UV peaks of undoped ZnO nanowires and doped nanonails are located at 379.5 and 385.4 nm, respectively. This red shift of 6 nm in the Sn doped samples indicates a reduction of the ZnO band gap caused by the Sn doping. The dominance of the green emission in the nanowires sample indicates that it exhibits a much higher defect concentration than the nanonails. 
ردمد : 0022-0248 
اسم الدورية : Journal of Crystal Growth 
المجلد : 327 
العدد : 1 
سنة النشر : 1432 هـ
2011 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Wednesday, February 8, 2012 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
وليد السيد محمودMahmoud, Waleed Eباحثدكتوراهw_e_mahmoud@yahoo.com
طلال صدقة الحربيAl-Harbi, Talal Sباحثدكتوراهtharbi1@yahoo.com

الملفات

اسم الملفالنوعالوصف
 32219.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث