Low-temperature synthesis of nanocrystalline NiCuZn ferrite and the effect of Cr substitution on its electrical properties
Low-temperature synthesis of nanocrystalline NiCuZn ferrite and the effect of Cr substitution on its electrical properties
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : In this study, nano-sized ferrites of compositions (Ni0.6Cu 0.20Zn0.20Fe2-xCrxO4), where x=01.0, were synthesized through nitratecitrate auto-combustion method at relatively low temperature. XRD revealed the formation of nano-sized ferrite particles with cubic spinel structure. An exception was obtained for samples with Cr content ≤0.2, where weak diffraction peaks attributed to the presence of CuO and Fe2O3 were appeared. The average crystallite sizes are much dependent on the chromium content and were found to decrease with its increase. The lattice parameter (a) slightly decreases with Cr substitution, which can be explained on the basis of the relative ionic radii of Cr3 and Fe3 ions. X-ray density was found also to decrease slightly with increase in chromium content, which indicates lower densification by the addition of Cr. FT-IR measurements show the characteristic ferrite bands. The Mssbauer spectra varied from Zeeman sextets to a relaxed doublet by increase in Cr content, which indicates a decrease in the hyperfine field at the octahedral site. Electrical property measurements revealed that Cr3 ions do not participate in conduction process but limit the degree of Fe3O2-Fe3 conduction resulting in a decrease in the conductivity and increase in conduction activation energy. 
ردمد : 0304-8853 
اسم الدورية : Journal of Magnetism and Magnetic Materials 
المجلد : 322 
العدد : 20 
سنة النشر : 1431 هـ
2010 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, October 30, 2011 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
محمد عبدالفتاح جبلGabal, Mohamed Aباحثدكتوراهmgabalabdonada@yahoo.com
ياسر محمد العنقريAl Angari, Y MباحثدكتوراهYALANGARI@kau.edu.sa

الملفات

اسم الملفالنوعالوصف
 31192.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث