Nanosized spinel oxide catalysts for CO-oxidation prepared via CoMnMgAl quaternary hydrotalcite route
Nanosized spinel oxide catalysts for CO-oxidation prepared via CoMnMgAl quaternary hydrotalcite route
 
الموضوع : كيمياء 
لغة الوثيقة : الانجليزية 
المستخلص : Catalytic activity of the Co-Mn-Mg-Al mixed oxide spinel catalysts was examined in CO oxidation by O2. The prepared catalysts were characterized by chemical analysis (ICP), infrared spectroscopy (FTIR), thermal analysis (TG, DTG), powder X-ray diffraction (XRD), surface area measurements, and scanning electron microscopy (SEM).The calcined hydrotalcite-like precursor was composed of spinel-like Co-Mn-Mg-Al mixed oxide as the only XRD crystalline phases. The nanosized spinel oxide catalysts produced by calcination of hydrotalcites showed higher SBET than CoMn-hydrotalcite samples as calcination led to dehydroxylation and carbonate decomposition of anions in interlayer spaces. All the catalysts showed 100% CO conversion at high temperature even those calcined at 800 °C. A catalyst with Co/Mn = 4 and calcined at 500 °C showed 100% CO conversion at 160 °C. Moreover, this catalyst exhibited quite good durability without deactivation in 60 h stability test. 
ردمد : 09258388 
اسم الدورية : Journal of Alloys and Compounds 
المجلد : 493 
العدد : 1-2 
سنة النشر : 1431 هـ
2010 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, April 12, 2010 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
محمد مختارMokhtar, Mohammed باحثدكتوراهmmoustafa@kau.edu.sa
سليمان ناصر باسهلBasahel, Suliman Naserباحثدكتوراهsbasahel@kau.edu.sa
ياسر محمد العنقريAl Angari, Y MباحثدكتوراهYALANGARI@kau.edu.sa

الملفات

اسم الملفالنوعالوصف
 26460.pdf pdfAbstract

الرجوع إلى صفحة الأبحاث