تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : Hierarchical ZnO nanostructures: Growth and optical properties Hierarchical ZnO nanostructures: Growth and optical properties   الموضوع : فيزياء  لغة الوثيقة : الانجليزية  المستخلص : Growth of hierarchical ZnO nanostructures composed of ZnO nanoneedles have been achieved via simple thermal evaporation process by using metallic zinc powder in the presence of oxygen at low temperature of 460°C on silicon substrate without the use of any kind of metal catalysts or additives. It is confirmed by detailed structural studies that the as-grown hierarchical nanostructures are single crystalline with a wurtzite hexagonal phase and nanoneedles of these structures are grown along the c-axis in the [0001] direction. The Raman-scattering analysis substantiates a wurtzite hexagonal phase with a good crystal quality for the as-grown products. Room-temperature photoluminescence (PL) exhibits a strong UV emission at 380 nm confirming the excellent optical properties of as-synthesized hierarchical structures. A plausible growth mechanism is also proposed to clearly understand the growth process of the synthesized structures. Copyright © 2008 American Scientific Publishers All rights reserved.  ردمد : 1533-4880  اسم الدورية : Journal of Nanoscience and Nanotechnology, Volume 8, Issue 12, December 2008, Pages 6355-6360  المجلد : 80  العدد : 12  سنة النشر : 2008 هـ 2008 م  عدد الصفحات : 6  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Thursday, October 15, 2009  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني Umar, A Umar, A باحث دكتوراه   Al Hajry, A Al Hajry, A باحث دكتوراه   صالح هديهد سلمان الحنيطي Al-Heniti باحث دكتوراه salheniti@kau.edu.sa Hahn, Y.-B Hahn, Y.-B باحث دكتوراه   الرجوع إلى صفحة الأبحاث